Stability of acid volcanic glasses in alkaline solutions: Understanding their potential to participate in the alkali-silica reaction
Autor
Locati, Francisco
Pérez Marfil, Paula M.
Marfil, Silvina A.
Lescano, Leticia
Metadata
Mostrar registro completoDescrição
Experimental laboratory tests were performed using volcanic glasses from Argentina of variable chemical composition and texture, in 1 N KOH, NaOH, Ca(OH)2 and combined NaOH + KOH + Ca(OH)2 solutions, at 40 °C and up to 10 weeks. The initial materials were characterized by petrography, chemical analysis, XRD, FT-IR and DSC-TGA. The reaction progress was evaluated by XRD, and the final products studied by SEM-EDS. The reactivity of the most reactive glass is attributed to a combination of its high porosity/permeability and alteration degree (indirectly assessed by the volatile mass loss up to ~250 °C). The glass silica content and Ca/(Al+Si) ratio could be other factors affecting the glass reactivity; however, more studies are needed to understand the influence of these variables.Fil: Locati, Francisco. CICTERRA (CONICET-UNC); Argentina
Fil: Locati, Francisco. Universidad Católica de Córdoba. Faculty of Engineering; Argentina
Fil: Pérez Marfil, Paula M. Universidad Nacional del Sur. Geology Department - CGAMA (CIC-UNS); Argentina
Fil: Marfil, Silvina A. Universidad Nacional del Sur. Geology Department - CGAMA (CIC-UNS); Argentina
Fil: Lescano, Leticia. Universidad Nacional del Sur. Geology Department - CGAMA (CIC-UNS); Argentina