dc.contributor.authorLiberto R.C.N.
dc.contributor.authorMagnabosco R.
dc.contributor.authorAlonso-Falleiros N.
dc.date.accessioned2019-08-20T00:17:36Z
dc.date.available2019-08-20T00:17:36Z
dc.date.issued2011
dc.identifier.citationLiberto, Rodrigo César Nascimento; Magnabosco, Rodrigo; ALONSO-FALLEIROS, Neusa. Selective corrosion of 550°C aged Cu10Ni 3Al 1.3Fe alloy in NaCl aqueous solution. Corrosion Science, n. 5, p. 1976-1982, 2011.
dc.identifier.issn0010-938X
dc.identifier.urihttps://repositorio.fei.edu.br/handle/FEI/2275
dc.description.abstractThis work studied the electrochemical behavior of a solution treated or 550°C aged Cu10Ni-3Al-1.3Fe alloy, in 0.01M NaCl aqueous solution, through potentiodynamic polarization in both stagnant condition or under erosion process. Results showed the occurrence of a passivity break potential (Epb), related to the beginning of the denickelification process, which occurred as a localized attack under stagnant electrolyte. Under erosion conditions localized denickelification was not observed, despite of the presence of Epb. This could indicate that selective corrosion of Ni, which caused the observed Epb, occurred as a dissolution-redeposition process, with removal of the Cu deposits during erosion process. © 2011 Elsevier Ltd.
dc.relation.ispartofCorrosion Science
dc.rightsAcesso Restrito
dc.titleSelective corrosion of 550°C aged Cu10Ni-3Al-1.3Fe alloy in NaCl aqueous solution
dc.typeArtigo


Arquivos deste item

ArquivosTamanhoFormatoVisualização

Este item aparece na(s) seguinte(s) coleção(s)

Mostrar registro simples


© AUSJAL 2022

Asociación de Universidades Confiadas a la Compañía de Jesús en América Latina, AUSJAL
Av. Santa Teresa de Jesús Edif. Cerpe, Piso 2, Oficina AUSJAL Urb.
La Castellana, Chacao (1060) Caracas - Venezuela
Tel/Fax (+58-212)-266-13-41 /(+58-212)-266-85-62

Nuestras redes sociales

facebook Facebook

twitter Twitter

youtube Youtube

Asociaciones Jesuitas en el mundo
Ausjal en el mundo AJCU AUSJAL JESAM JCEP JCS JCAP