[pt] TENACIDADE DE MATERIAIS COMPÓSITOS NÃO CONVENCIONAIS

FLAVIO DE ANDRADE SILVA

[en] TOUGHNESS OF NON CONVENTIONAL COMPOSITE MATERIALS

dc.contributor	KHOSROW GHAVAMI
dc.creator	FLAVIO DE ANDRADE SILVA
dc.date	2004-08-12
dc.date.accessioned	2022-09-21T21:44:01Z
dc.date.available	2022-09-21T21:44:01Z
dc.identifier	https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=5271@1
dc.identifier	https://www.maxwell.vrac.puc-rio.br/colecao.php?strSecao=resultado&nrSeq=5271@2
dc.identifier	http://doi.org/10.17771/PUCRio.acad.5271
dc.identifier.uri	https://hdl.handle.net/20.500.12032/42826
dc.description	[pt] O objetivo deste trabalho foi avaliar as propriedades mecânicas, físicas e microestruturais de materiais compósitos cimentícios reforçados por fibras naturais e de laminados de bambu. O trabalho experimental foi direcionado para a determinação da tenacidade. Para se determinar a tenacidade foram utilizados três tipos de ensaios: impacto Charpy, impacto balístico e flexão em 3 pontos. Após os ensaios, a superfície de fratura dos corpos-de-prova foi analisada por microscopia eletrônica de varredura (MEV). Esta análise microestrutural serviu para determinar os modos de fratura e validar as hipóteses feitas nos modelos matemáticos utilizados. Foram usados modelos adaptados da literatura para a determinação da tenacidade e os valores teóricos obtidos foram confrontados com os experimentais. Determinou-se também através de modelos encontrados na literatura a tensão interfacial de todas as fibras utilizadas nesta pesquisa. Os modelos empregados para calcular a tenacidade e a tensão de adesão interfacial, se mostraram eficientes e válidos. Em segundo plano, porém não menos importante, ficou a determinação das propriedades térmicas dos materiais utilizados. Foram efetuados ensaios de condutividade térmica do compósito e ensaios termogravimétricos das fibras vegetais e do bambu. Os compósitos cimentícios foram reforçados por diferentes fibras naturais: polpa refinada de bambu (CPB), polpa de sisal (CPS), polpa de eucalipto (CPE), fibras curtas de sisal (CPFS) e wollastonita (CPW). As proporções das polpas de bambu, sisal e eucalipto utilizadas como reforço nas matrizes cimentícias foram de 8 por cento e 14 por cento em relação à massa do cimento, a da fibra curta de sisal (25 mm) foi de 3 por cento em relação ao volume e a da wollastonita foi de 11,5 por cento em relação à massa. Compóstios híbridos feitos com wollastonita e polpa de bambu (CPBW) foram também produzidos apenas variando a proporção da polpa de bambu em 8 por cento e 14 por cento e mantendo fixa a da wollastonita em 11,5 por cento. Como uma tentativa de se melhorar a resistência ao impacto, laminados CPB/AL foram também fabricados colando duas chapas de alumínio (liga 5052 H34) de espessura 0,8 mm em ambas às faces dos compósitos reforçados por fibra de bambu, formando assim compósitos sanduíche (CPBA). O bambu Moso (Phyllostachys heterocycla pubescens) com 5 anos de idade foi usado para fabricação dos laminados de bambu, sendo tratado com água fervida para a prevenção de ataques biológicos. Técnicas para a extração do laminado a partir de seu formato natural foram estudadas estabelecendo suas vantagens e desvantagens. Para o ensaio de impacto foram utilizados corpos-de-prova com dimensão nominal de 120 mm x 15 mm x 6 mm perfazendo um total de 18 corpos-de-prova. Para o de flexão foram realizados ensaios com uma lâmina simples de bambu (BL) e bambu laminado colado (BLC) com 3 camadas de lâminas dispostas ortogonalmente. Os resultados dos testes de impacto Charpy e flexão em 3 pontos comprovaram a boa tenacidade do bambu laminado quando submetido a cargas de impacto (42,54 kJ/m2) e a cargas estáticas (19,77 kJ/m2 para o laminado e 17,63 kJ/m2 para o laminado colado). Compósitos sanduíche constituídos de alumínio e laminados de bambu foram também fabricados. Estes foram analisados através de ensaios de impacto balísticos seguindo as recomendações da norma NIJ 0101.04. Observações no microscópico eletrônico de varredura foram realizadas para se analisar os mecanismos de falha dos laminados.
dc.description	[en] The main objective of this work was to evaluate the mechanical, physical and microestructure properties of cementitious composite materials and bamboo laminates. The experimental program was focused on the determination of toughness. Three diferent types of tests were performed in order to establish it: Charpy impact, ballistic impact and three point bending test. After the tests, the fractured surface of the failed test specimens was observed using a Scanning Electron Microscope (SEM) to establish the failure mode. Mathematical models adapted from the available literature were used to determine the toughness from which the values were confronted to the ones obtained experimentally. It was also determined by mathematical models the interfacial bond stress of all fibers used in this research. The two models, used in the toughness and interfacial bond stress calculation, showed to be efficient, providing valid results. In second plan, but not less important, was the determination of the materials thermal properties. Thermal conductivity tests of the composites and thermogravimetry of the fibers and bamboo were performed. The cementitious composites were reinforced by different natural fibers: refined bamboo pulp (CPB), sisal pulp (CPS), eucalyptus pulp (CPE), short sisal fibers (CPFS) and wollastonite. The mass fraction of bamboo, sisal and eucalyptus pulp studied were 8 percent and 14 percent. For the wollastonite fiber the mass fraction studied was 11.5 percent and for the short sisal fiber a 3 percent volume fraction was studied. Hybrid composites made with wollastonite and bamboo pulp (CPBW) were also produced varying the bamboo fraction mass to 8 percent and 14 percent but keeping constant to 11.5 percent the wollastonite mass fraction. The slurry de-watering process was used in the production of all composites described before. To reduce the adverse effects of weathering on the cellulose fibers and to improve the impact load and flexural resistance of the composite, aluminum thin sheets were used to produce a sandwich composite lamina with the CPB, which was denominated as CPBA. Compound Adhesive gel from Otto Baumgart which is a type of epoxy was used to fix the aluminum sheets on the CPB. The use of aluminum has proved to give much higher impact resistance results when compared to the CPB ones. The 5 years old Moso bamboo (Phyllostachys heterocycla pubescens), which was previously treated in boiled water to eliminate biological agents, was used to produce the bamboo laminates. Techniques were developed to extract bamboo laminates from its natural form, establishing its advantages and disadvantages. For the Charpy impact test, a total of 18 specimens with nominal dimensions of 120 mm x 15 mm x 6 mm were tested. Laminated (BL) and 3 layer cross ply laminated bamboo (BLC) were tested in bending. A total of 9 specimens were tested per bamboo configuration. The BL specimens had nominal dimensions of 120 mm x 30 mm x 6 mm and the BLC were 120 mm x 30 mm x 17 mm. The results demonstrated the good toughness of bamboo laminates when subject to dynamic (42.54 kJ/m2) and to static load (19.77 kJ/m2 for the laminate and 17.63 kJ/m2 for the cross ply laminate). Aluminum thin sheets were again used to make sandwich composites, but now using the bamboo laminate (BLCA). The BLCA was tested using the ballistic impact test following the standard NIJ 0101.04. Analysis on the Scanning Eléctron Microscope (SEM) were performed in order to establish the laminate s failure mechanisms.
dc.language	pt
dc.publisher	MAXWELL
dc.subject	[pt] BAMBU
dc.subject	[pt] IMPACTO CHARPY
dc.subject	[pt] TENACIDADE
dc.subject	[pt] PROPRIEDADES TERMICAS
dc.subject	[pt] LAMINADOS
dc.subject	[pt] IMPACTO BALISTICO
dc.subject	[pt] MATRIZ CIMENTICIA
dc.subject	[pt] FIBRAS NATURAIS
dc.subject	[en] BAMBOO
dc.subject	[en] CHARPY IMPACT
dc.subject	[en] TOUGHNESS
dc.subject	[en] THERMAL PROPERTIES
dc.subject	[en] LAMINATES
dc.subject	[en] BALLISTIC IMPACT
dc.subject	[en] CEMENTITIOUS MATRIX
dc.subject	[en] NATURAL FIBRES
dc.title	[pt] TENACIDADE DE MATERIAIS COMPÓSITOS NÃO CONVENCIONAIS
dc.title	[en] TOUGHNESS OF NON CONVENTIONAL COMPOSITE MATERIALS
dc.type	TEXTO

Files in this item

Files	Size	Format	View
There are no files associated with this item.

This item appears in the following Collection(s)

Documentos - PUC-RIO

Show simple item record