Evaluation of microstructural effects on the degree of sensitization (DOS) of a UNS S31803 duplex stainless steel aged at 475°C
dc.contributor.author | De Melo E.B. | |
dc.contributor.author | Magnabosco R. | |
dc.date.accessioned | 2019-08-20T00:17:37Z | |
dc.date.available | 2019-08-20T00:17:37Z | |
dc.date.issued | 2015 | |
dc.identifier.citation | BARBOSA DE MELO, EVELIN; Magnabosco, Rodrigo. EVALUATION OF MICROSTRUCTURAL EFFECTS ON THE DEGREE OF SENSITIZATION (DOS) OF A UNS S31803 DUPLEX STAINLESS STEEL AGED AT 475ºC. CORROSION, v. 71, n. 12, p. 1490-1499, 2015. | |
dc.identifier.issn | 0010-9312 | |
dc.identifier.uri | https://repositorio.fei.edu.br/handle/FEI/2286 | |
dc.description.abstract | © 2015, NACE International.In this study, microstructural and electrochemical behavior of a UNS S31803 duplex stainless steel aged at 475°C were investigated. Hardness values increased with aging at 475°C and evidence of alpha prime (α′) phase formation was confirmed by transmission electron microscopy analysis. Double loop electrochemical potentiokinetic reactivation measurements in a 2 M H2SO4 + 0.5 M NaCl + 0.01 M KSCN solution showed an increase in the degree of sensitization values, mainly for the sample aged for 360 h at 475°C. Moreover, the results suggest that α′ phase formation occurred via spinodal decomposition mechanism. | |
dc.relation.ispartof | Corrosion | |
dc.rights | Acesso Restrito | |
dc.title | Evaluation of microstructural effects on the degree of sensitization (DOS) of a UNS S31803 duplex stainless steel aged at 475°C | |
dc.type | Artigo |